 note = {application/pdf, The polymerization of epichlorhydrin with sodium hydroxide was studied at 80℃ in　bulk.　When　used 100 mole?％　sodium　hydroxide （based　on　monomer），the　maximum degree of conversion （27％） was oberved and the polymer yield increased according to the reaction time up to 200 min. The highest yield was 61.5％ on these conditions. The most part of the chlorine was removed during polymerization ; the polymer had lower chlorine content than Zilkha’s polymer; its residual chlorine in polymer could not be completely removed by alkaline hydrolysis. All the polymers appeared to be crosslinked. The presence of C=O and C＝C was detected by infrared spectra and other analyses. 0n the basis of these observations， the structure of the polymer and reaction mechanism was assumed. The polymer had the capacity of sorption as sillica gel.},